Product Details:
|
| Features: | Cn Bonding Layer Improve The Initial And Final Bonding Strength | Product Name: | Conveyor Rubber Ceramic Pulley Lagging With Cold Vulcanizing Cn Bonding Layer |
|---|---|---|---|
| Application: | Installed On Conveyor Pulley | Usage: | Prevent Belt Slippage, Extend Service Life Of Pulley And Belt |
| Thickness: | 12mm, 15mm, 20mm, 25mm, Etc | Width: | 500mm, 200mm |
| Length: | 1050mm, 1200mm, 1400mm, 2550mm, 10 Meter, Customized | Advantage: | Reliable Factory, Resonable Price, Proven Quality |
| Ceramic Tiles: | 95% Al2O3 Ceramics | ||
| Highlight: | Cold Vulcanizing Rubber Ceramic Pulley Lagging,Cn Bonding Layer Ceramic Pulley Lagging,Cold Vulcanizing ceramic rubber lagging |
||
Conveyor Rubber Ceramic Pulley Lagging With Cold Vulcanizing Cn Bonding Layer
Description:
Ceramic pulley lagging is installed on the conveyor drive pulley to prevent belt slippage and extend the service life of conveyor belt and pulley. The alumina ceramic tiles help in proper grip of the belt under wet, muddy or any other such arduous conditions.
Ceramic pulley lagging is specially suited for pulleys where slippage and excessive wear and tear problems make normal rubber lagging ineffective.
Ceramic Pulley Lagging With Cn Bonding Layer
Ceramic Pulley Lagging in pieces, custom-made sizes are available
Ceramic Pulley Lagging can also be produced in rolls. 10 meter per roll
Technical Data
| Alumina Ceramic Tile | ||
| Aluminum Oxide | % | 95 |
| Specific Gravity | g/cm3 | 3.7 |
| Vickers Hardness | HV(30) | 1010 |
| Fracture Toughness | MPa•m1/2 | 3.6 |
| Rubber Compound | ||
| Tensile Strength | MPa | 20 |
| Elongation At Break | % | 600 |
| Hardness | Shore A | 63+/-5 |
| Abrasion Loss | mm3 | 110 |
| CN Layer Bonding Strength | kN/m | 13 |